BLISTERS DON'T MATTER !!
In as much as there has always been some concern with the common place occurance of "blistering" when surveying vessels, and since this has always been a source of contention and cause of innumerable questions, we thought that we would include the following article on our website to give some perspective, regarding this phenomenon.
OFFSHORE ATLANTIC YACHTS is pleased to announce that Mr. Jan de Groot has given us exclusive permission to reprint his article which was published in Pacific Yachting. His biography appears at the bottom of this article.
I'm going to say this right here, right now: "Gelcoat blisters don't matter!" There, I said it, at the risk of being called an opinionated, stubborn Dutchman!
Probably, I inherited those terrible qualities from my Grandfather who built two fiberglass boats in his shipyard in Holland in the early fifties, This he did, despite predictions of doom and gloom, forecasted by numerous experts. Until that time, the yard had been using respectable materials such as wood and steel.
I remember those first two plastic boats because they created quite an upheaval amongst the workers in the yard. "The old man has gone off his rocker", they said. The boats were named after my two aunts, Cornelia and Josephine. They were (the boats, not my aunts) 37 foot, full keel sailing yachts, designed by Sparkman and Stephens.
But, I do not want to blame my Grandfather, rest his soul, for my blister problem. My problem is that gelcoat blisters do not appear to be a problem. Yet, everyone says, "they are!" Many articles have been written by experts about their destructive qualities. They are referred to as the pox, cancer and all sorts of other horrible diseases which will cause certain death when inflicted upon a human being. "Don't buy a boat with the pox", they say, "it will delaminate" - another scary term. Some say blisters should be repaired by removing layers of laminates from the hull and then to be laid over with new layers of glass. Peeling machines are now being marketed to strip the layers from the hull. As a result, thousands of dollars are being spent on blister repair. I have seen figures as high as twenty thousand dollars for a thirty foot boat.
Why are gelcoat blisters considered to be such a disastrous problem? Based on what research and by whose authority?
To answer that question we have to examine the business of pleasure boating as a whole. In North America, pleasure boating and almost everything that is related to it, is pretty much a wide open, non regulated and uncontrolled industry. As opposed to the building of a house, you don't need building permits, there is no building code, there is no building inspector. Anyone can build, use any type of design, any kind of material. Cardboard? Why not? No one will stop you, as long as you have the appropriate amount of life jackets, fire extinguishers, navigation lights and baling devices, you will probably pass the voluntary Coast Guard inspection, providing the boat doesnt sink before it reaches the Coast Guard dock. Anyone can sell boats, no license required, hang up a shingle and you are a boat surveyor - again no license required. And then, anyone, no age limit, no experience required, can take that eighty foot cardboard boat, powered by twin super charged one thousand horse power engines, out for a spin on the beckoning wild blue yonder. You think Star Trek is the last frontier? No way, the boating business is. Isn't it wonderful? Yes, most definitely, it is. Pleasure boating is probably the only ungoverned pastime left on this polluted earth. No helmets, no license, no seat belts, and you're allowed to smoke on your boat too! You can even have a sip of brew while driving, although, that is pushing it a little bit. But, you can get away with it as long as you don't hit anybody. I'm all for it! However, because of this, the boating industry attracts a lot of self appointed experts. The government doesn't appoint, so we do it ourselves. So, the experts are where the boats are. The number of experts closely equal the number of boats. Ask one question and you're bound to receive a multitude of answers and opinions. Most of the experts cast spells of doom and gloom and readily relate some tale of woe that has happened to so and so to add credit to their advice. Bear in mind that a gloomy view of something demands more attention and sounds more impressive. There is always a knowledgeable answer, let's face it, a reply such as "Gosh I don't know", or, "I have to read up on that", just doesn't cut it!
Now let's get back to blisters. I have also formed an opinion about blisters, just like all the other experts. I will back up that opinion by reasoning. Here is my case:
The first time I had to deal with a gelcoat blister problem was in the late sixties. Until then, I had not encountered it before, most certainly not to the extent as in that particular case. As a result I did a lot of research and talked to a lot of people in the fiberglass trade. I did not get any deeply researched scientific answers other than the fact that the gelcoat was blistering, as in "paint blistering from wood or steel". In other words, it's coming off! Perhaps it was because the surface underneath it was not prepped properly, or it was not dry when the gelcoat was applied or, it is just plain tired and worn and needs to be done again. Since that time I have seen a lot of boat bottoms. These busy days, through my Company, I see or hear of and deal with as many as close to a thousand per year. Therefore, I think I can safely say that I see more "bottoms" than most and that includes boat yards. It is therefor, I think, safe to say that it is likely that I have seen, tapped, probed, dug into and caressed more blisters than most. Yet, after having had a working part in the boating industry since the days well before fiberglass, I have never encountered a fiberglass boat that was in any way structurally damaged or unsafe to operate as a result of gelcoat blisters. To silence any critics of this statement I suggest they produce or point out a boat of normal solid fiberglass construction which has become structurally unsound and unsafe to be operated for it's intended service as a result of gelcoat blisters. If they can, I'll eat it!
Gelcoat blister problems can occur due to three basic reasons:
1. The use of type of resins, such as fire retardant resins. In this case blisters are generally also apparent above the waterline of the hull and on the superstructure. It is not caused by water. It can not be fixed because the problem is within the composition of the hull laminates.
2. Poor building procedures. The fiberglass cloth is not stored properly and has become damp prior to layup. The result is intermittent and generally poor bonding of the resins with the cloth and the gelcoat. The blisters may appear above as well as below the waterline. As a rule the vessel will have internal delamination of the fiberglass layers and may or may not have any gelcoat blisters. The delaminated areas may show up as very large blisters and the outer layer of the blister will be thick since it may contain several laminates. This is a structural problem and is difficult if not impossible to repair.
3. Water migrates through the gelcoat. Blisters are located under the water line and sometimes located along the water line only. When punctured, the blisters contain a colorless liquid which is acidic.
Number 1. Is mainly encountered in a certain series and make of production boat. The manufacturer corrected the problem several years ago.
Number 2. Is rare and not typical of production type boats. I have encountered it sporadically. In each instance the boats were manufactured by companies who normally produce a very good product.
Number 3. This is the one occurring frequently and which is the one most of us have seen evidence of and which is the topic of this article.
Let's examine the procedure. Water migrates through the gelcoat. This takes time. The speed depends on the thickness and or the porosity of the gelcoat. In fresh water, the effect can be quicker because fresh water is thinner and lighter than salt water.
Lessons to be learned from this are: Do not sand or scrape the gelcoat prior to painting with anti fouling paint because it makes the gelcoat porous and thinner. (I have been preaching against sanding and scraping for years. Now, some manufacturers, such as Hunter Marine, do not allow sanding of the gelcoat. It will void the warranty against blistering of the gelcoat. Perhaps my cries of agony have been heard!)
Older boats are less likely to get blisters because their gelcoat is thicker, as a matter of fact, so is their entire lay-up, thicker that is. Some older boats will never get blisters because they were built differently.
The laminates of most glass boats consist of mat and woven roving impregnated with resin. Roving are strands of glass fibers which are woven together as in a piece of textile. Mat, on the other hand is made up of chopped up strands of glass fibers which are held together by a starch like substance. In each case, the whole thing becomes a solid piece when saturated with resin.
Woven roving has tear strength. It is difficult to pull apart. Mat has no tear strength and can easily be pulled apart. It acts as a filler, making the hull thicker and stiffer. It has some impact strength, but that is all.
Early fiberglass boats were built over male molds, up side down. The inner layer of the glass was the first layer, the outer layer the last. As a rule, the last layer was woven roving, not mat. Gelcoat was applied last, as a finish. (The very early boats had no gelcoat at all. The hull was faired, sanded, and then painted) In some cases, especially with hard chine hulls, the hull was gelcoated and tightly wrapped with plastic. When the gelcoat was cured, the plastic was removed, and bingo, a smooth finish!
As building techniques progressed, hulls were built in female molds. It was discovered that the gelcoat could be applied first to the inside of the mold and then the layers of roving and mat were laid over that. It was soon discovered that, upon close examination, the pattern of the woven roving, which was adjacent to the gelcoat, would show, especially if the gelcoat was thin.. This is called "print through". This caused the manufacturers to reverse the procedure and put the mat next to the gelcoat instead of woven roving. ( Mat has no pattern and a much finer texture) There is only one problem - the fibers in mat are held together with a starch like substance. I believe this to be the culprit of the blisters to some extent and the reason of the damage caused by the blisters to a great extent. The general consensus amongst chemists is that when water migrates through the gelcoat and remains there for some time without circulation, (REMEMBER THIS) that a chemical reaction takes place which produces acid. It appears that the acid dissolves the starch like substance which in turn dislodges the resin and possibly evacuates this through the process of osmosis. In other words, it slowly disperses back out through the gelcoat to set up a balance with the surrounding water. When the blister becomes the approximate size of a quarter, as a rule, when opened up, a small cavity can be seen in the outer laminate, which is the layer of mat. What one sees are the loose glass fibers, the resin is absent. Providing the boat was built properly in the first place, meaning same is not kept afloat on this layer of mat, in which case it would have broken up well before the blisters appear, these cavities do not weaken the structure. I have never seen the woven roving affected by this process, which again proofs the fact that it is the acid combined with the binding agent in the mat, and not the resin, which is the culprit.
Remember that in order for the chemical reaction to take place, the water has to have been trapped under the gelcoat for some time without circulation. It therefore follows that if the blisters are punctured at an early stage, before they have been able to cause any damage, there will be circulation, thus, the acid will not form or get to a stage where it can be harmful. In any event, as I said, the damage, if any, is restricted to the outer layer of mat, which is not a structural component of the hull laminates anyhow and is there strictly for cosmetic purposes. In fact, many fiberglass boats have been built and repair jobs have been done, without a coating of gelcoat. Obviously, there is no need to spend a fortune by peeling layers of glass from the hull. At most, to achieve a cosmetically pleasing appearance, the blister can be removed by sand blasting or grinding to remove the gelcoat, or by peeling of the gelcoat only, faired with filler and then sealed with any of the products readily available and suitable for that purpose. Or, otherwise, just grind the blisters off and paint!
Whatever you do, do not strip layers of laminates from the hull. This will structurally harm the vessel. There is no guarantee that the new layers applied will stick properly. In many cases where I have seen this done, the new layers are blistering, then you do have a problem because the hull laminates are now weakened!
A fiberglass hull does not absorb water. Core material, yes, but solid glass, no! Glass and resins are inert. There is no space for water. That plastic bucket that has contained water for many years, is as dry as a bone when the surface is wiped and dried. I put a humidity meter on a water bucket which my wife had used for many years in the paddock of her horse. I emptied it, gave it a good wipe and left in the sunshine for twenty minutes. The humidity reading was 5 percent, exactly the same as a brand new one.
It is often claimed that a hull has absorbed water and has therefore become heavier. These findings are based on readings with a humidity meter. Both statements are inaccurate. The humidity meter in the wrong hands is a dangerous instrument. The thing works by means of conductivity. The electrical current takes the shortest route through material with the least amount of resistance. A humidity meter cannot be used over anti fouling paint because it is more conductive than fiberglass. Fire retardant resins cannot be metered for the same reason. Damp cloth, interior liners, paint, steel fuel tanks, water tanks, wooden frames and floors, if installed against or near the fiberglass measured, will throw the meter off scale. I started using a humidity meter in 1981 and I am still learning. Further more, what is often misunderstood is that the meter gives a reading of RELATIVE humidity. Not solid water content. Listen to the weather report, the announcer may state that the relative humidity is 65 percent. That does not mean that we are standing up to our necks in water. In fact, I was told by an employee of Sovereign Moisture Meters that when the meter's needle is at 100 percent, the actual water content is equivalent to one drop of water per cubic foot of fiberglass.
The question of weight is another mystery. The statement goes, "the glass has absorbed water and therefore has become heavier." In the first place, glass cannot absorb water, it could only absorb water if there was vacant space in the laminates. (poorly built and delaminated) or, if water has displaced those areas previously occupied by fiberglass. In other words due to some mysterious process, water has removed the fiberglass from the hull and taken its place. Let's assume for argument's sake that this is possible. Water is now occupying space that was previously occupied by fiberglass. Well, it now becomes a question of specific gravity. All I know is that if I dump a piece of fiberglass in the ocean, it sinks like a stone. Yet, the water which I pour from a bucket seems to just sort of float around. To me that indicates that water is lighter than fiberglass. In other words, if I substituted portions of fiberglass from my boat with water, the boat should become lighter, never heavier!
Coatings of paint, epoxy and gelcoat will blister. Paint will blister on wooden boats and houses, epoxy coatings blister on steel and ferro cement boats, gelcoat will blister on fiberglass boats. What does all this mean?
When a boat has blisters, I find I have to depreciate its value, not because of her being unsound or unsafe, but due to misinformation. The general public will either not buy that boat, or expect a price reduction. The result? There are a lot of good boats out there which are going cheaply because they have blisters, but will provide the same enjoyment and are as safe as those with the smooth bottoms. For racing sailors, there is actually an advantage to having a boat with blisters. If they loose the race they can blame it on the blisters rather their sailing skill.
How long does fiberglass last? Nobody knows, it hasn't been around long enough. Perhaps my Grandfather can give us some idea. Not long ago I was in Grenada, West Indies. I was looking for an ex crew member of mine who had opened up a bar on Hog Island. I went there to look him up, but he had gone away on some errand. As I stood waiting I scanned the boats in the anchorage. One sail boat looked awfully familiar. I borrowed a dinghy and went in for a closer look. I rowed around the boat and eventually could not stop myself from being rude and climbed on board. I checked her over pretty carefully and concluded she was in pretty good shape and obviously ready and trimmed to take her owners on the next leg of their voyage. As I rowed away, I stopped to give her one last look. The yacht had swung away, showing her transom. On it was her name, it read, Josephine. "Not bad", I thought, "she is now almost fifty years old and she keeps going and going and going..."
) Jan de Groot
About the author
Jan de Groot was born and educated in Holland. He comes from a long line of seagoing ancestors. His great grandfather was a sea captain as was his grandfather who was born at sea. The family operated a shipyard in Holland and much of Jan's youth was spent in the yard which was his favourite playground.
As was traditional with the male members of the family, he was destined to either become actively involved in the yard, or follow in the footsteps of his grandfathers and roam the seven seas. Jan did both. At age 14 he was crew on delivery of a sailing yacht from Holland to Durban, South Africa. While studying at the Merchant Naval Academy, he worked in the shipyard during holidays. When he graduated he went to sea on merchant vessels. He served as a deck officer in the Dutch Merchant Navy, and later as Captain in the British Merchant Marine.
In the late sixties Jan ended up in the West Indies where he operated his 114 foot sailing yacht "Ring Andersen" in the luxury charter yacht trade. He has chronicled his Caribbean experiences in a book called "No Shoes Allowed".
Jan now alternates residence between Vancouver, Canada, and Grenada. He is a marine surveyor and an author. Other books under his name are: "Buying The Right Boat" and "Gone to Come Back", the latter is the sequel to "No Shoes Allowed". He is also a regular contributor of articles about boating to various magazines and a regular writer for the monthly magazine "Caribbean Compass". His column "Tips and Tricks" is featured in Pacific Yachting Magazine. He frequently makes "guest-speaker" appearances at Yacht Clubs and Power Squadrons.
Web site: www.degrootmarine.com
OFFSHORE ATLANTIC YACHTS
Covering the U.S., Canada, the Entire Caribbean|
AND THE WORLD !!!
World Headquarters, FL 33455, United States